DESCRIPTION
This product is made of excellent inorganic mineral gelling materials, siliceous materials and high molecular polymers as the main base materials, and is compounded with a variety of additives through a unique production process. It can be used by adding water and stirring on site. It is a polymer modified mortar with high water retention rate, high strength, high adhesion and good anti-sagging properties.
Strong adhesion; low shrinkage, no cracks;
Good workability and good anti-slip properties;
Fast setting, good repair effect; good water resistance.
Composition Information
Appearance: Uniform, no lumps | Initial flow in truncated cone: 300 mm | Flow in truncated cone after 20 min: 272 mm | Flexural strength (6 h): 3.2 MPa |
Flexural strength (24 h): 6.4 MPa | Flexural strength (28 d): 11.7 MPa | Compressive strength (6 h): 13.3 MPa | Compressive strength (24 h): 32.0 MPa |
| Compressive strength (28 d): 61.2 MPa | Tensile bond strength (24 h): 1.45 MPa | Tensile bond strength (28 d): 2.71 MPa | Dry shrinkage： 0.085% |
Interfacial flexural strength: 3.60 MPa | Dimensional change rate under restricted conditions: | Applicable standard: |